SAN DIEGO, CA.-
A new technology could dramatically improve the safety of lithium-ion batteries that operate with gas electrolytes at ultra-low temperatures. Nanoengineers at the University of California San Diego
developed a separatorthe part of the battery that serves as a barrier between the anode and cathodethat keeps the gas-based electrolytes in these batteries from vaporizing. This new separator could, in turn, help prevent the buildup of pressure inside the battery that leads to swelling and explosions.
By trapping gas molecules, this separator can function as a stabilizer for volatile electrolytes, said Zheng Chen, a professor of nanoengineering at the UC San Diego Jacobs School of Engineering who led the study.
The new separator also boosted battery performance at ultra-low temperatures. Battery cells built with the new separator operated with a high capacity of 500 milliamp-hours per gram at -40 C, whereas those built with a commercial separator exhibited almost no capacity. The battery cells still exhibited high capacity even after sitting unused for two monthsa promising sign that the new separator could also prolong shelf life, the researchers said.
The team published their findings June 7 in Nature Communications.
The advance brings researchers a step closer to building lithium-ion batteries that can power vehicles in the extreme cold, such as spacecraft, satellites and deep-sea vessels.
This work builds on a previous study published in Science by the lab of UC San Diego nanoengineering professor Ying Shirley Meng, which was the first to report the development of lithium-ion batteries that perform well at temperatures as low as -60 C. What makes these batteries especially cold hardy is that they use a special type of electrolyte called a liquefied gas electrolyte, which is a gas that is liquefied by applying pressure. It is far more resistant to freezing than a conventional liquid electrolyte.
But theres a downside. Liquefied gas electrolytes have a high tendency to go from liquid to gas. This is the biggest safety issue with these electrolytes, said Chen. In order to use them, a lot of pressure must be applied to condense the gas molecules and keep the electrolyte in liquid form.
To combat this issue, Chens lab teamed up with Meng and UC San Diego nanoengineering professor Tod Pascal to develop a way to liquefy these gassy electrolytes easily without having to apply so much pressure. The advance was made possible by combining the expertise of computational experts like Pascal with experimentalists like Chen and Meng, who are all part of the UC San Diego Materials Research Science and Engineering Center (MRSEC).
Their approach makes use of a physical phenomenon in which gas molecules spontaneously condense when trapped inside tiny, nanometer-sized spaces. This phenomenon, known as capillary condensation, enables a gas to become liquid at a much lower pressure.
The team leveraged this phenomenon to build a battery separator that would stabilize the electrolyte in their ultra-low temperature batterya liquefied gas electrolyte made of fluoromethane gas. The researchers built the separator out of a porous, crystalline material called a metal-organic framework (MOF). Whats special about the MOF is that it is filled with tiny pores that are able to trap fluoromethane gas molecules and condense them at relatively low pressures. For example, fluoromethane typically condenses under a pressure of 118 psi at -30 C; but with the MOF, it condenses at just 11 psi at the same temperature.
This MOF significantly reduces the pressure needed to make the electrolyte work, said Chen. As a result, our battery cells deliver a significant amount of capacity at low temperature and show no degradation.
The researchers tested the MOF-based separator in lithium-ion battery cellsbuilt with a carbon fluoride cathode and lithium metal anodefilled with fluoromethane gas electrolyte under an internal pressure of 70 psi, which is well below the pressure needed to liquefy fluoromethane. The cells retained 57% of their room temperature capacity at -40 C. By contrast, cells with a commercial separator exhibited almost no capacity with fluoromethane gas electrolyte at the same temperature and pressure.
The tiny pores of the MOF-based separator are key because they keep more electrolyte flowing in the battery, even under reduced pressure. The commercial separator, on the other hand, has large pores and cannot retain the gas electrolyte molecules under reduced pressure.
But tiny pores are not the only reason the separator works so well in these conditions. The researchers engineered the separator so that the pores form continuous paths from one end to the other. This ensures that lithium ions can still flow freely through the separator. In tests, battery cells with the new separator had 10 times higher ionic conductivity at -40 C than cells with the commercial separator.
Chens team is now testing the MOF-based separator on other electrolytes. We are seeing similar effects. We can use this MOF as a stabilizer to adsorb various kinds of electrolyte molecules and improve the safety even in traditional lithium batteries, which also have volatile electrolytes.
Paper: Sub-Nanometer Confinement Enables Facile Condensation of Gas Electrolyte for Low-Temperature Batteries. Co-authors include Guorui Cai*, Yijie Yin*, Dawei Xia*, Amanda A. Chen, John Holoubek, Jonathan Scharf, Yangyuchen Yang, Ki Kwan Koh, Mingqian Li, Daniel M. Davies and Matthew Mayer, UC San Diego; and Tae Hee Han, Hanyang University, Seoul, Korea.
This work was supported by NASAs Space Technology Research Grants Program (ECF 80NSSC18K1512), the National Science Foundation through the UC San Diego Materials Research Science and Engineering Center (MRSEC, grant DMR-2011924) and startup funds from the Jacobs School of Engineering at UC San Diego. This work was performed in part at the San Diego Nanotechnology Infrastructure (SDNI) at UC San Diego, a member of the National Nanotechnology Coordinated Infrastructure, which is supported by the National Science Foundation (grant ECCS-1542148). This research used resources of the National
Energy Research Scientific Computing Center, a DOE Office of Science User Facility supported by the Office of Science of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231. This work also used the Extreme Science and Engineering Discovery Environment (XSEDE), and the Comet and Expanse supercomputers at the San Diego Supercomputing Center, which is supported by National Science Foundation (grant ACI-1548562).